Shanghai Huitian New Material Co., Ltd
Created with Pixso.
बोली
Created with Pixso. घर > उत्पादों >
इलेक्ट्रॉनिक चिपकने वाला
>

5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio

5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio

5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio
  • 5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio
  • 5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio
  • 5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio

5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio

उत्पाद विवरण:
उत्पत्ति के प्लेस: चीन
ब्रांड नाम: Huitian
प्रमाणन: ROHS REACH
मॉडल संख्या: 5290
विस्तार से जानकारी
उत्पत्ति के प्लेस:
चीन
ब्रांड नाम:
Huitian
प्रमाणन:
ROHS REACH
मॉडल संख्या:
5290
रंग भाग ए:
लाल
रंग भाग बी:
सफ़ेद
श्यानता भाग ए:
4,500 ~ 7,000 एमपीए · एस
चिपचिपाहट भाग बी:
4,000 ~ 6,500 एमपीए · एस
मिश्रण अनुपात:
1: 1
घनत्व भाग ए:
2.7 ~ 2.8 ग्राम/एमएल
घनत्व भाग बी:
2.7 ~ 2.8 ग्राम/एमएल
शेल्फ जीवन:
6 महीने
कार्य -तापमान:
-50-200 ℃
प्रमुखता देना:
5290R thermal conductive potting compound , silicone potting compound 2W/mK , 1:1 mix ratio electronic potting
ट्रेडिंग जानकारी
न्यूनतम आदेश मात्रा:
1000kg
मूल्य:
बातचीत योग्य
पैकेजिंग विवरण:
20 किग्रा/सेट: ए: 10 किग्रा/बकेट, बी: 10 किग्रा/बकेट।
आपूर्ति की क्षमता:
100एमटी/माह
उत्पाद वर्णन
5290R 2W High Thermal Conductive 1:1 Mix Red/White Silicone, UL94V-0, -50°C To 200°C
Ideal for electronics encapsulation, automotive module sealing, sensor potting & circuit board protection.
Product Overview
The 5290R(A9B9) is a high-performance, two-part addition-type potting silicone rubber designed for electronic and electrical applications. Combining exceptional thermal conductivity with excellent flow properties, this product offers both thermal management and mechanical protection. The red/white 1:1 mixing ratio ensures simple and consistent application.
Key Applications
  • Inverter Inductance: Provides thermal management and mechanical protection
  • Military Power Supplies: Ensures reliable performance in harsh environments
  • Communication Modules: Offers moisture-proof and shockproof protection
  • General Electronics: Suitable for transformers, capacitors, and PCBs
Product Features
High Thermal Conductivity
2 W/m*K thermal conductivity for efficient heat dissipation
Excellent Flow Properties
Viscosity range: 4,500-7,000 mPa*s (Part A), 4,000-6,500 mPa*s (Part B)
Dual Curing Mechanism
Cures at room temperature (≤6 hours) or accelerated with heat (≤30 minutes at 80°C)
Superior Insulation
Dielectric strength ≥13 KV/mm, volume resistivity ≥1.0×10^12 Ω*cm
Wide Temperature Range
Maintains elasticity from -50°C to 200°C
Safety Compliance
UL94V-0 flame retardant, RoHS compliant
Technical Specifications
Physical Properties Before Curing (25 ±2℃, 60%±5%RH)
Appearance (A) - Red flow
Appearance (B) - White flow
Viscosity (A) mPa*s 4,500~7,000
Viscosity (B) mPa*s 4,000~6,500
Density (A) g/cm^3 2.7~2.8
Density (B) g/cm^3 2.7~2.8
Curing Properties (A:B=1:1)
Operating Time min 130±70
Curing Time (25℃) h ≤6
Curing Time (80℃) min ≤30
Physical Properties After Curing (A:B=1:1)
Hardness Shore A 35~45
Dielectric Strength KV/mm ≥13
Volume Resistivity Ω*cm ≥1.0×10^12
Dielectric Constant (1.2MHz) - ≥2.8
Thermal Conductivity W/m*K 2±0.2
Application Instructions
Preparation
Stir Part A and Part B separately to ensure uniformity before mixing.
Mixing
Weigh components in 1:1 ratio and mix thoroughly for homogeneous consistency.
Defoaming
  • Natural Defoaming: Allow 20-30 minutes for air bubble release
  • Vacuum Defoaming: 5-10 minutes at -0.1 MPa vacuum
Potting
Apply to clean, dry surfaces while mixture maintains good flowability.
Curing
Room temperature or heat accelerated curing available. Higher temperatures reduce curing time.
Packaging & Storage
Packaging: 5290RA9 20kg/barrel, 5295RB9 20kg/barrel
Storage: 8-28°C in cool, dry location. 6 month shelf life when properly stored.
Safety Information
Store in sealed containers away from children. Avoid contact with N, P, S organic compounds and Sn, Pb, Hg, As ionic compounds which may inhibit curing. Consult MSDS for complete safety details.
5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio 0
Application example of 5290R Silicone Potting Compound
5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio 1
5290R Silicone Potting Compound packaging
5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio 2
Technical specifications of 5290R Silicone Potting Compound

टैग:

Created with Pixso.
डाउनलोड करना Created with Pixso.
नंबर 251, Wenji रोड, मात्सुए जिला, शंघाई चीन E-mail: intlsales@huitian.net.cn Tel: 18817338191 Tel: 18817338191
चीन में सबसे बड़ा अनुसंधान एवं विकास और उत्पादन चिपकने वाला आपूर्तिकर्ता
8618817338191
18817338191
गोपनीयता नीति | साइट मैप | चीन अच्छी गुणवत्ता फोटोवोल्टिक चिपकने वाला आपूर्तिकर्ता. 2016-2025 industryglue.com . सर्वाधिकार सुरक्षित।